Cladding in optical fibers is one or more layers of materials of lower refractive index in intimate contact with a core material of higher refractive index.

The cladding causes light to be confined to the core of the fiber by total internal reflection at the boundary between the core and cladding. Light propagation within the cladding is typically suppressed for most fibers. However, some fibers can support cladding modes in which light propagates through the cladding as well as the core. Depending upon the quantity of modes that are supported, they are referred to as multi-mode fibers and single-mode fibers. Improving transmission through fibers by applying a cladding was discovered in 1953 by Dutch scientist Bram van Heel.

History

The fact that transmission through fibers could be improved by applying a cladding was discovered in 1953 by van Heel, who used it to demonstrate image transmission through a bundle of optical fibers. Early cladding materials included oils, waxes, and polymers. Lawrence E. Curtiss at the University of Michigan developed the first glass cladding in 1956, by inserting a glass rod into a tube of glass with a lower refractive index, fusing the two together, and drawing the composite structure into an optical fiber.

Modes

A cladding mode is a mode that is confined to the cladding of an optical fiber by virtue of the fact that the cladding has a higher refractive index than the surrounding medium, which is either air or the primary polymer overcoat. These modes are generally undesired. Modern fibers have a primary polymer overcoat with a refractive index that is slightly higher than that of the cladding, so that light propagating in the cladding is rapidly attenuated and disappears after only a few centimeters of propagation. An exception to this is double-clad fiber, which is designed to support a mode in its inner cladding, as well as one in its core.

Advantages

In the production of glass fibers, there will inevitably be surface irregularities (ex. pore and cracks) that will scatter light when struck and lessen the total travel distance of the light. The inclusion of a glass cladding greatly reduces the attenuation caused by these surface irregularities. This is due to the light scattering less at the glass/glass interface than it would have at the glass/air interface for a fiber without cladding. The two primary factors that allow for this are the smaller change in index of refraction seen between two surfaces of glass, as well as surface irregularities on the cladding not interfering with the light beams. The inclusion of glass cladding is also an improvement over just applying a polymer coating, as glass will typically be stronger, more homogenous, and cleaner. Additionally, the inclusion of a cladding layer also allows for the usage of smaller glass fiber cores. With most glass fibers have a cladding that raises the total outer diameter to 125 microns.

Effect on numerical aperture

The numerical aperture of a multimode optical fiber is a function of the indices of refraction of the cladding and the core:

${\displaystyle {\rm {{NA}={\sqrt {n_{\rm {core}}^{2}-n_{\rm {clad}}^{2}}}}}}$

The numerical aperture allows for the calculation of the acceptance angle of incidence at the fiber interface. Which will give the maximum angle at which the incidence light can enter the core and maintain total internal reflection:

${\displaystyle {\rm {{NA}=\sin(\theta _{A})}}}$

By combining both of these equations it can be seen in the diagram above how ${\displaystyle \theta _{A}}$ is a function of ${\displaystyle n_{1}}$ and ${\displaystyle n_{2}}$, where ${\displaystyle n_{1}}$ is the index of refraction of the core and ${\displaystyle n_{2}}$

${\displaystyle n_{2}}$ is the index of refraction of the cladding.

Recent developments

Due to the relatively greater transmission of light they offer, fiber optic cores and claddings are usually made from highly purified silica gas. Certain impurities can be added to impart various properties, such as increasing transmission distance or improving fiber flexibility. There has been significant work done in improving these properties within the last several years.

References

 This article incorporates public domain material from Federal Standard 1037C. General Services Administration. Archived from the original on January 22, 2022. (in support of MIL-STD-188).

1. "Optical Fibers". labman.phys.utk.edu. Retrieved May 26, 2023.
2. ^ Zlatanov, Nikola (March 2017). "Introduction to Fiber Optics Theory". doi:10.13140/RG.2.2.29183.20641.
3. "Fiber 101" (PDF). iBwave Solutions. Archived (PDF) from the original on November 26, 2019.
4. ^ Hecht, Jeff (2004). City of light : the story of fiber optics. Oxford: Oxford University Press. pp. 55–70. ISBN 978-0-19-802676-1. OCLC 60543677.
5. ^ Crisp, John (2005). Introduction to fiber optics. Barry J. Elliott. Amsterdam: Newnes. ISBN 978-0-7506-6756-2. OCLC 162130345.
6. Ghatak, Ajoy; Thyagarajan, K. (1998), "Introduction: The fiber optics revolution", Introduction to fiber optics, Cambridge: Cambridge University Press, pp. 1–8, doi:10.1017/cbo9781139174770.002, ISBN 9781139174770, retrieved November 27, 2021
7. ^ "The FOA Reference For Fiber Optics - Optical Fiber". www.thefoa.org. Retrieved April 10, 2016.
8. Bass, Michael (2010). Handbook of optics. McGraw-Hill. ISBN 978-0-07-163314-7. OCLC 904221758.

This article needs additional or more specific categories. Please help out by adding categories to it so that it can be listed with similar articles. (October 2024)

• Fiber optics
• Optics