Annealing (glass) - Misplaced Pages

(Redirected from Annealed glass) Process for relieving stress in manufactured glass For other uses, see Annealing (disambiguation).

This article needs additional citations for verification. Please help improve this article by adding citations to reliable sources. Unsourced material may be challenged and removed.
Find sources: "Annealing" glass – news · newspapers · books · scholar · JSTOR (July 2018) (Learn how and when to remove this message)

Annealing is a process of slowly cooling hot glass objects after they have been formed, to relieve residual internal stresses introduced during manufacture. Especially for smaller, simpler objects, annealing may be incidental to the process of manufacture, but in larger or more complex products it commonly demands a special process of annealing in a temperature-controlled kiln known as a lehr. Annealing of glass is critical to its durability. Glass that has not been properly annealed retains thermal stresses caused by quenching, which will indefinitely decrease the strength and reliability of the product. Inadequately annealed glass is likely to crack or shatter when subjected to relatively small temperature changes or to mechanical shock or stress. It even may fail spontaneously.

To anneal glass, it is necessary to heat it to its annealing temperature, at which its viscosity, η, drops to 10 Poise (10 dyne-second/cm). For most kinds of glass, this annealing temperature is in the range of 454–482 °C (849–900 °F), and is the so-called stress-relief point or annealing point of the glass. At such a viscosity, the glass is still too hard for significant external deformation without breaking, but it is soft enough to relax internal strains by microscopic flow in response to the intense stresses they introduce internally. The piece then heat-soaks until its temperature is even throughout and the stress relaxation is adequate. The time necessary for this step varies depending on the type of glass and its maximum thickness. The glass then is permitted to cool at a predetermined rate until its temperature passes the strain point (η = 10 Poise), below which even microscopic internal flow effectively stops and annealing stops with it. It then is safe to cool the product to room temperature at a rate limited by the heat capacity, thickness, thermal conductivity, and thermal expansion coefficient of the glass. After annealing is complete the material can be cut to size, drilled, or polished without risk of its internal stresses shattering it.

At the annealing point (η = 10 Poise), stresses relax within several minutes, while at the strain point (η = 10 Poise) stresses relax within several hours. Stresses acquired at temperatures above the strain point, and not relaxed by annealing, remain in the glass indefinitely and may cause either short-term or much delayed failure. Stresses resulting from cooling too rapidly below the strain point largely are considered temporary, although they may be sufficient to cause short-term failure.

References

E. F. Collins (1921) Electrically heated glass annealing lehr. Journal of the American Ceramic Society 4 (5), pp. 335–349
"All About Glass". www.cmog.org. Corning Museum of Glass. 9 December 2011.
Werner Vogel: "Glass Chemistry"; Springer-Verlag Berlin and Heidelberg GmbH & Co. K; 2nd revised edition (November 1994), ISBN 3-540-57572-3

v t e Glass science topics
Basics	Glass Glass transition Supercooling
Formulation	AgInSbTe Bioglass Borophosphosilicate glass Borosilicate glass Ceramic glaze Chalcogenide glass Cobalt glass Cranberry glass Crown glass Flint glass Fluorosilicate glass Fused quartz GeSbTe Gold ruby glass Lead glass Milk glass Phosphosilicate glass Photochromic lens glass Silicate glass Soda–lime glass Sodium hexametaphosphate Soluble glass Tellurite glass Thoriated glass Ultra low expansion glass Uranium glass Vitreous enamel Wood's glass ZBLAN
Glass-ceramics	Bioactive glass CorningWare Glass-ceramic-to-metal seals Macor Zerodur
Preparation	Annealing Chemical vapor deposition Glass batch calculation Glass forming Glass melting Glass modeling Ion implantation Liquidus temperature sol–gel technique Viscosity Vitrification
Optics	Achromat Dispersion Gradient-index optics Hydrogen darkening Optical amplifier Optical fiber Optical lens design Photochromic lens Photosensitive glass Refraction Transparent materials
Surface modification	Anti-reflective coating Chemically strengthened glass Corrosion Dealkalization DNA microarray Hydrogen darkening Insulated glazing Porous glass Self-cleaning glass sol–gel technique Tempered glass
Diverse topics	Conservation and restoration of glass objects Glass-coated wire Safety glass Glass databases Glass electrode Glass fiber reinforced concrete Glass ionomer cement Glass microspheres Glass-reinforced plastic Glass cloth Glass-to-metal seal Porous glass Pre-preg Prince Rupert's drops Radioactive waste vitrification Windshield Glass fiber